A2 Stainless Steel (ISO 3506 group A2 (304 / 1.4301), commonly supplied A2-70) is the most common stainless group for indoor and general outdoor fasteners. When countersunk head grooved pins are specified in this grade, the dimensions remain per ISO 8747; the material determines corrosion behavior (good general corrosion resistance) and the service temperature range (approx. -200 °C to +400 °C, subject to the property class and the joint). Both are covered below with the size table.
Why Choose A2 Stainless Steel for Countersunk Head Grooved Pins
The most common stainless group for indoor and general outdoor fasteners. For countersunk head grooved pins, this matters when good general corrosion resistance is the primary requirement.
Mechanical & Physical Properties
| Grade designation | ISO 3506 group A2 (304 / 1.4301), commonly supplied A2-70 |
|---|---|
| Magnetic response | Largely non-magnetic |
| Service temperature | approx. -200 °C to +400 °C, subject to the property class and the joint |
| Corrosion characteristic | Good general corrosion resistance |
Galvanic & Galling Considerations
For stainless countersunk head grooved pins the compatibility question is galvanic rather than galling: joined to aluminum or galvanized steel in wet service, stainless drives corrosion of the less-noble metal. Isolate with a coating, sleeve or non-conductive washer where the joint sees moisture. Note also that stainless is softer than hardened carbon steel, so where the part carries a wear or shear duty, check the load against the grade before substituting.
Comparable Grades
For Countersunk Head Grooved Pins, the alternative stainless grade is A4 (316). Choose A2 (304) for general use and A4 (316) wherever chlorides are present; the molybdenum in A4 is the whole difference. Remember that stainless is the corrosion answer, not the strength answer — for load, look at class 8.8 or 10.9 instead.
Using Stainless Fasteners in Aluminum
Expect the aluminum to corrode, not the fastener — stainless sits higher in the galvanic series, so the aluminum is the one that gives up material. A small fastener in a thick section spreads the loss over a large area and is usually fine; a large fastener in thin sheet concentrates it and is not. Keep water out of the joint, or isolate the two metals with a nylon or coated washer and a sealant.
Sizes of Countersunk Head Grooved Pins Available in A2 Stainless Steel
| Nominal diameter d (mm) | d_1_max (mm) | d_1_min (mm) | d_k_max (mm) | d_k_min (mm) | d_2 (mm) | c (mm) | Length range l (mm) | Reference standard |
|---|---|---|---|---|---|---|---|---|
| 1.4 mm | 1.4 | 1.35 | 2.7 | 2.3 | 1.5 | 0.42 | 3~6 | ISO 8747 |
| 1.6 mm | 1.6 | 1.55 | 3 | 2.6 | 1.7 | 0.48 | 3~8 | ISO 8747 |
| 2 mm | 2 | 1.95 | 3.7 | 3.3 | 2.15 | 0.6 | 4~10 | ISO 8747 |
| 2.5 mm | 2.5 | 2.425 | 4.6 | 4.2 | 2.7 | 0.75 | 4~12 | ISO 8747 |
| 3 mm | 3 | 2.925 | 5.45 | 4.95 | 3.2 | 0.9 | 5~16 | ISO 8747 |
| 4 mm | 4 | 3.9 | 7.25 | 6.75 | 4.25 | 1.2 | 6~20 | ISO 8747 |
| 5 mm | 5 | 4.9 | 9.1 | 8.5 | 5.25 | 1.5 | 8~25 | ISO 8747 |
| 6 mm | 6 | 5.9 | 10.8 | 10.2 | 6.3 | 1.8 | 8~30 | ISO 8747 |
| 8 mm | 8 | 7.85 | 14.4 | 13.6 | 8.3 | 2.4 | 10~40 | ISO 8747 |
| 10 mm | 10 | 9.85 | 16 | 14.9 | 10.35 | 3 | 12~40 | ISO 8747 |
| 12 mm | 12 | 11.8 | 19 | 17.7 | 12.35 | 3.6 | 16~40 | ISO 8747 |
| 16 mm | 16 | 15.8 | 26 | 23.7 | 16.4 | 4.8 | 20~40 | ISO 8747 |
| 20 mm | 20 | 19.8 | 31.5 | 30.7 | 20.5 | 6 | 25~40 | ISO 8747 |
Dimensions are independent of the material: every size above is available in A2 Stainless Steel.
Custom manufacturing · Made to drawing
Need this pin in a grade that is not listed?
A2 Stainless Steel is one of the grades the catalog describes. End form, hardness and surface finish are all variable; the diameter tolerance is the one that decides the process. Made by cold heading or turning.
Minimum order from 2,000 pieces; samples within 7 days of drawing approval.