Property Class 8.8 Steel All-Metal Lock Nuts combine the dimensional form of ISO 7042 / DIN 980 with the material properties of grade ISO 898-1 property class 8.8: requires plating (zinc) for corrosion protection, magnetic, service range commonly limited to approx. +300 °C; confirm against the coating and the load. This page summarizes the grade data, its corrosion behavior in service, the comparable grades, and the sizes supplied.
Why Choose Property Class 8.8 Steel for All-Metal Lock Nuts
The workhorse medium-carbon alloy class for structural joints. For all-metal lock nuts, this matters when requires plating (zinc) for corrosion protection is the primary requirement.
Mechanical & Physical Properties
| Grade designation | ISO 898-1 property class 8.8 |
|---|---|
| Magnetic response | Magnetic |
| Service temperature | commonly limited to approx. +300 °C; confirm against the coating and the load |
| Corrosion characteristic | Requires plating (zinc) for corrosion protection |
Galvanic & Galling Considerations
For all-metal lock nuts in steel, the dominant compatibility issue is hydrogen embrittlement at high property classes (10.9 and above) when electroplated. Plating must be followed by an appropriate baking treatment, or a non-electroplated finish (mechanical zinc, zinc flake) should be substituted.
Comparable Grades
For All-Metal Lock Nuts, class 10.9 or 12.9 is the comparable strength step. Move up when the joint preload approaches the proof load of the current class; move down when the joint is over-specified. For corrosion-critical service, switch to stainless A2 or A4.
Sizes of All-Metal Lock Nuts Available in Property Class 8.8 Steel
| Size | Pitch (mm) | Width across flats s (mm) | Nut height m (mm) | Reference standard | Notes |
|---|---|---|---|---|---|
| M5 | 0.8 | 8.0 | 6.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M6 | 1.0 | 10.0 | 7.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M8 | 1.25 | 13.0 | 9.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M10 | 1.5 | 16.0 | 11.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M12 | 1.75 | 18.0 | 13.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M14 | 2.0 | 21.0 | 15.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M16 | 2.0 | 24.0 | 17.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M18 | 2.5 | 27.0 | 19.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M20 | 2.5 | 30.0 | 21.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M24 | 3.0 | 36.0 | 24.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M30 | 3.5 | 46.0 | 30.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |
| M36 | 4.0 | 55.0 | 36.0 | ISO 7042 / DIN 980 | Deformed-top locking, high-temperature capable |