M10 Left-Hand Thread Hex Bolts are manufactured to DIN 933 with a coarse thread pitch of 1.5 mm. This page lists the controlling dimensions for the M10 size — head geometry, width across flats, matching spanner size — together with the clearance hole, tapping drill and tightening torque used at assembly.
M10 Dimensional Row (DIN 933)
| Thread size | Pitch (mm) | Across flats s (mm) | Across corners e (mm) | Head height k (mm) | Thread direction | Common length range (mm) | Reference standard |
|---|---|---|---|---|---|---|---|
| M10 | 1.5 | 17 | 18.90 | 6.4 | Left-hand | 16~100 | DIN 933 LH |
Spanner & Drive for M10 Left-Hand Thread Hex Bolts
Drive geometry for M10 Left-Hand Thread Hex Bolts is given by the row above; match the tool to the listed values.
Hole Sizes for M10
| Coarse-thread pitch (ISO 724) | 1.5 mm |
|---|---|
| Through-hole / clearance (ISO 273 medium) | 11 mm |
| Tapping drill, coarse thread | 8.5 mm |
Tightening Torque for M10
| Class 8.8 (dry, ~µ 0.125) | ≈ 48 Nm |
|---|---|
| Class 10.9 (dry, ~µ 0.125) | ≈ 71 Nm |
| Class 12.9 (dry, ~µ 0.125) | ≈ 83 Nm |
Indicative dry-joint values. Lubrication can lower the required torque by 15–25%. Always confirm against the joint design, especially when going up a strength class.
Proof Load & Strength for M10
| Tensile stress area As (ISO 724) | 58 mm² |
|---|---|
| Proof load, class 8.8 | 34 kN |
| Proof load, class 10.9 | 48 kN |
| Proof load, class 12.9 | 56 kN |
| Min. ultimate tensile load, class 8.8 | 46 kN |
Proof load = tensile stress area × the proof stress Sp of the class, per ISO 898-1 — Sp is a lower figure than the yield stress Rp0.2 and the two are not interchangeable. The stress area is computed from this size's own diameter and pitch, so a fine-pitch designation gives the fine-pitch figure. Design the joint so the working preload stays below the proof load of the class selected.
M10 Left-Hand Thread Hex Bolts Weight
A steel M10 left-hand thread hex bolts at the listed 16,100 mm length weighs approximately 9,939 g each — about 9,939 kg per 1,000 pieces. Stainless A2/A4 weighs roughly the same (density 7.9–8.0 g/cm³).
Actual weight varies slightly with head form, thread and finish; use this figure for freight estimation only.
Mating Parts for M10
For M10, pair with a M10 hex nut (ISO 4032 / DIN 934) and, where used, a M10 flat washer (ISO 7089 / DIN 125A) under the head and under the nut.
When to Step Up or Down from M10
When the joint preload approaches the proof load of M10 class 8.8, step up to M12 class 8.8 (or move to M10 class 10.9). When the joint is over-specified, M8 often saves weight and cost without losing the safety margin.
Custom manufacturing · Made to drawing
Need left-hand thread hex bolts in a size this table does not list?
This page covers M10 left-hand thread hex bolts. Where the standard stops, the drawing takes over: fine pitches, left-hand threads, partial threading, and property classes above the catalogued grade where material and heat treatment allow. Made by cold heading or hot forging.
Minimum order from 2,000 pieces; samples within 7 days of drawing approval.