M30 is one of the standard coarse-thread sizes for stud bolt, double-end under GB/T 15389 / DIN 938. The sections below reproduce the dimensional row, list the matching tools and hole sizes, and summarize where this size is normally specified.
M30 Dimensional Row (GB/T 15389 / DIN 938)
| Thread size | Pitch (mm) | Length L (mm) | Engagement depth bm (mm) | Material | Reference standard |
|---|---|---|---|---|---|
| M30 | 3.5 | 240 | 45 | Cl. 8.8 alloy steel | DIN 939 / GB/T 901 |
Hole Sizes for M30
| Coarse-thread pitch (ISO 724) | 3.5 mm |
|---|---|
| Through-hole / clearance (ISO 273 medium) | 33 mm |
| Tapping drill, coarse thread | 26.5 mm |
Tightening Torque for M30
| Class 8.8 (dry, ~µ 0.125) | ≈ 1443 Nm |
|---|---|
| Class 10.9 (dry, ~µ 0.125) | ≈ 2055 Nm |
| Class 12.9 (dry, ~µ 0.125) | ≈ 2405 Nm |
Indicative dry-joint values. Lubrication can lower the required torque by 15–25%. Always confirm against the joint design, especially when going up a strength class.
Proof Load & Strength for M30
| Tensile stress area As (ISO 724) | 561 mm² |
|---|---|
| Proof load, class 8.8 | 336 kN |
| Proof load, class 10.9 | 465 kN |
| Proof load, class 12.9 | 544 kN |
| Min. ultimate tensile load, class 8.8 | 465 kN |
Proof load = tensile stress area × the proof stress Sp of the class, per ISO 898-1 — Sp is a lower figure than the yield stress Rp0.2 and the two are not interchangeable. The stress area is computed from this size's own diameter and pitch, so a fine-pitch designation gives the fine-pitch figure. Design the joint so the working preload stays below the proof load of the class selected.
Mating Parts for M30
For M30, pair with a M30 hex nut (ISO 4032 / DIN 934) and, where used, a M30 flat washer (ISO 7089 / DIN 125A) under the head and under the nut.
Custom manufacturing · Made to drawing
Need stud bolt, double-end in a size this table does not list?
This page covers M30 stud bolt, double-end. Dimensions, material, finish and form are specified from the drawing — a bolt outside the standard range is a variation on existing tooling rather than a new design. Made by cold heading or hot forging.
Minimum order from 2,000 pieces; samples within 7 days of drawing approval.